PCTG材料 FX100 Eastman Tritan 不含双酚A BAP 伊斯曼官方datasheet物性表 TDS
PCTG材料 Eastman Tritan 共聚聚酯 FX100伊斯曼官方物性表 TDS
与我们联系索取Eastman官方 PCTG FX100 物性表 datasheet
PCTG材料 Eastman Tritan™ FX100
Copolyester
Eastman Chemical Company
产品说明：
Eastman Tritan™ FX100 is an amorphous copolyester that combines excellent clarity and toughness with outstanding heat and chemical resistance. Films manufactured from this new-generation copolyester can be thermoformed without pre-drying and with a wide processing window that allows for product designs that reflect intricate detail. Eastman Tritan™ FX100 copolyester may be used in repeated use food contact articles under United States Food and Drug Administration (FDA) regulations. Eastman Tritan™ FX100 copolyester is certified to NSF/ANSI Standard 51 for Food Equipment Materials.
物性信息：
|
基本信息 |
|
|
特性 |
|
|
用途 |
|
|
机构评级 |
|
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
1.19 |
g/cm³ |
ASTM D792 |
|
吸水率 (23°C, 24 hr, 0.250 mm) |
0.50 |
% |
ASTM D570 |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
耐磨耗性 (23°C) 1 |
23haze |
% |
ASTM D1044 |
|
薄膜 |
额定值 |
单位制 |
测试方法 |
|
Carbon Dioxide Permeability (23°C, 254.0 µm) 2 |
150 |
cm³·mm/m²/atm/24 hr |
ASTM D1434 |
|
Elmendorf Tear Strength |
|
|
|
|
MD : 23°C, 250.0 µm |
5 |
N |
ASTM D1922 |
|
TD : 23°C, 250.0 µm |
6 |
N |
|
|
PPT Tear Resistance |
|
|
ASTM D2582 |
|
MD : 23°C, 250.0 µm |
42 |
N |
ASTM D2582 |
|
TD : 23°C, 250.0 µm |
56 |
N |
ASTM D2582 |
|
抗撕裂蔓延性 3 |
|
|
ASTM D1938 |
|
MD : 23°C, 250.0 µm |
410 |
gf |
ASTM D1938 |
|
TD : 23°C, 250.0 µm |
310 |
gf |
ASTM D1938 |
|
光学性能 |
额定值 |
单位制 |
测试方法 |
|
UV Transmittance (250.0 µm) 4 |
89 |
% |
|
|
补充信息 |
额定值 |
单位制 |
测试方法 |
|
Surface Energy |
|
|
ASTM D5946 |
|
Dispersive : 23°C, 250.0 µm |
39 |
dyne/cm |
ASTM D5946 |
|
Polar : 23°C, 250 mm |
8 |
dyne/cm |
ASTM D5946 |
|
Total : 23°C, 250.0 µm |
46 |
dyne/cm |
ASTM D5946 |
|
薄膜 |
额定值 |
单位制 |
测试方法 |
|
薄膜厚度 - 经测试 |
250 |
µm |
|
|
膜刺穿强度 5(250 µm) |
4.60 |
J |
ASTM D3763 |
|
割线模量 |
|
|
ASTM D882 |
|
MD : 250 µm |
1500 |
MPa |
ASTM D882 |
|
TD : 250 µm |
1400 |
MPa |
ASTM D882 |
|
抗张强度 |
|
|
ASTM D882 |
|
MD : 屈服, 250 µm |
41.0 |
MPa |
ASTM D882 |
|
TD : 屈服, 250 µm |
40.0 |
MPa |
ASTM D882 |
|
MD : 断裂, 250 µm |
59.0 |
MPa |
ASTM D882 |
|
TD : 断裂, 250 µm |
52.0 |
MPa |
ASTM D882 |
|
伸长率 |
|
|
ASTM D882 |
|
MD : 屈服, 250 µm |
7.0 |
% |
ASTM D882 |
|
TD : 屈服, 250 µm |
7.0 |
% |
ASTM D882 |
|
MD : 断裂, 250 µm |
180 |
% |
ASTM D882 |
|
TD : 断裂 |
200 |
% |
ASTM D882 |
|
落锤冲击 6 |
|
|
ASTM D1709A |
|
-30°C, 250 µm |
910 |
g |
ASTM D1709A |
|
23°C, 250 µm |
880 |
g |
ASTM D1709A |
|
裤型撕裂耐性 7 |
|
|
ISO 6383-1 |
|
MD : 250 µm |
11.0 |
N/mm |
ISO 6383-1 |
|
TD : 250 µm |
11.0 |
N/mm |
ISO 6383-1 |
|
透氧率 (23°C, 250 µm, 50% RH) |
32 |
cm³·mm/m²/atm/24 hr |
ASTM D3985 |
|
水气透过率 |
|
|
ASTM F1249 |
|
23°C, 100% RH, 250 µm |
4.0 |
g/m²/24 hr |
ASTM F1249 |
|
38°C, 100% RH, 250 µm |
11 |
g/m²/24 hr |
ASTM F1249 |
|
弹性体 |
额定值 |
单位制 |
测试方法 |
|
撕裂强度 |
|
|
ASTM D1938 |
|
开裂 8 |
12 |
kN/m |
ASTM D1938 |
|
开裂 9 |
13 |
kN/m |
ASTM D1938 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
熔融温度 |
110 |
°C |
|
|
线形热膨胀系数 - 流动 (23°C, 0.250 mm) |
9.0E-5 |
cm/cm/°C |
ASTM D696 |
|
比热 |
|
|
DSC |
|
60°C |
1700 |
J/kg/°C |
DSC |
|
100°C |
1900 |
J/kg/°C |
DSC |
|
150°C |
2200 |
J/kg/°C |
DSC |
|
200°C |
2400 |
J/kg/°C |
DSC |
|
250°C |
2600 |
J/kg/°C |
DSC |
|
光学性能 |
额定值 |
单位制 |
测试方法 |
|
光泽度 (60°, 250 µm) |
161 |
|
ASTM D2457 |
|
折射率 |
1.550 |
|
ASTM D542 |
|
透射率 (250 µm) |
92.0 |
% |
ASTM D1003 |
|
雾度 (250 µm) |
0.70 |
% |
ASTM D1003 |
|
黄度指数 (250 mm) |
0.50 |
YI |
ASTM D1925 |
|
备注 |
|
|
1 . |
average at 25 cycles |
|
2 . |
50% RH |
|
3 . |
254 mm/min |
|
4 . |
% Transmission at 380 nm |
|
5 . |
Dynatup, Total Energy |
|
6 . |
12.7 mm dia. head, 127 mm dia. clamp, 600 mm drop |
|
7 . |
200 mm/min |
|
8 . |
TD, 250 µm |
|
9 . |
MD, 250 µm |
Tritan™，全称Tritan Copolyester，中文名萃特， 是美国Eastman公司开发的新一代共聚酯。
例如，聚碳酸酯水解后会产生双酚A。现代医学研究认为，双酚A超过一定剂量或将影响人类健康（包括动物）， 如果长期摄入微量的双酚A，会造成内分泌系统混乱，非常有可能对生殖系统产生不良影响，破坏性别比例的平衡，因此部分国家和地区已经限制或禁用聚碳酸酯。
Tritan™的优点
1.不含BPA：伊斯曼Tritan™“在聚合生产过程中无BPA成分,在使用过程中也不会释放BPA，符合环保要求及FDA。
2.清晰透明：透光率>90%，雾度<1%，有水晶般的光泽。
3.优异的抗冲击强度：无缺口冲击不断,有缺口冲击强度因牌号不同在650-980J/m之间，可比美PC的冲击强度。•优秀的抗化、抗水解性能：Tritan ™"能抗洗涤剂、清洁剂、经类溶剂、油类、香水等腐蚀:在湿热的环境中能抗水解。
4.耐温高：低压热变形温度(HDT@0.455MPa)根据牌号不同在94℃-109℃之间。
5.流动性好：测试条件在2.16kgf压力,280熔体温度条件下,烧指(MI)根据牌号不同在15.3-29.5之间。
·容易成型加工：Tritan ™“的牌号可用注塑(injection)、挤出(extrusion)、吹塑(EEM)、注拉吹(ISBM)等各种方法加工。一般来说，用PC能正常生产的模具，无须改动便可用Tritan™”“来生产，生产周期时间非常接近。
6.容易二次加工：PCTG Tritan 可适用于的二次加工方法包括:UV胶水粘接、超声波熔接、表面印刷喷漆、表面真空电镀等。
7.制品残余应力小：注塑后，产品残余应力比PC小，无须再做后续退火处理。产品在使用过程中由于残余应力开裂的机会少，所以Tritan™制造出来的产品更加经久耐用。
Tritan™的市场应用
伊斯曼 PCTG Tritan™ 作为新一代共聚聚酯，经过Eastman多年的研发，已进入商业化应用阶段。其牌号已自成体系，以满足市场的各种需求。Eastman首先在欧美市场上进行了推广应用，Tritan TM凭着环保易加工等优良品质引起了欧美市场的积极响应，并取得了很大的成功。总体来说，Tritan™"可以适用于传统共聚聚酯的所有市场应用。在这里，我们将通过案例展示来着重介绍它替代PC的市场应用。