Ultramid 8231G HS is a heat stabilized, 15% glass fiber reinforced PA6 injection molding compound. It is also available in non-heat stabilized (Ultramid 8231) and/or pigmented versions. The glass fiber reinforcement enhances performance such as strength, stiffness and heat deflection temperature. The heat stabilizer system extends the properties at elevated temperatures. It also has excellent chemical resistance to greases, oils and hydrocarbons.
Applications
Ultramid 8231G HS is ideally suited for more demanding performance applications such as safety helmet parts, washers, gears, engine and motor parts, chutes, and higher temperature environments.
Ultramid® 8231G HS 物性表 工程塑料 PA66
基本信息 |
|
黄卡编号 |
|
填料/增强材料 |
|
添加剂 |
|
特性 |
|
用途 |
|
机构评级 |
|
RoHS 合规性 |
|
外观 |
|
形式 |
|
加工方法 |
|
多点数据 |
|
物理性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
比重 |
1.23 |
-- |
g/cm³ |
ASTM D792, ISO 1183 |
收缩率 - 流动 (3.18 mm) |
0.50 |
-- |
% |
|
吸水率 |
|
|
|
|
24 hr |
1.4 |
-- |
% |
ASTM D570 |
23°C, 24 hr |
1.4 |
-- |
% |
ISO 62 |
饱和 |
8.1 |
-- |
% |
ASTM D570 |
饱和, 23°C |
8.1 |
-- |
% |
ISO 62 |
平衡, 50% RH |
2.3 |
-- |
% |
ASTM D570 |
平衡, 23°C, 50% RH |
2.3 |
-- |
% |
ISO 62 |
硬度 |
干燥 |
调节后的 |
单位制 |
测试方法 |
洛氏硬度 (R 级) |
121 |
-- |
|
ASTM D785 |
机械性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
拉伸模量 |
|
|
|
ISO 527-2 |
-40°C |
5950 |
6600 |
MPa |
ISO 527-2 |
23°C |
5960 |
2640 |
MPa |
ISO 527-2 |
80°C |
2470 |
2300 |
MPa |
ISO 527-2 |
121°C |
2090 |
1900 |
MPa |
ISO 527-2 |
抗张强度 |
|
|
|
|
断裂, -40°C |
160 |
170 |
MPa |
ASTM D638, ISO 527-2 |
断裂, 23°C |
140 |
79.0 |
MPa |
ASTM D638 |
断裂, 80°C |
60.0 |
20.0 |
MPa |
ASTM D638, ISO 527-2 |
断裂, 121°C |
50.0 |
40.0 |
MPa |
ASTM D638, ISO 527-2 |
断裂, 23°C |
140 |
80.0 |
MPa |
ISO 527-2 |
伸长率 |
|
|
|
|
断裂, -40°C |
3.0 |
4.0 |
% |
ASTM D638 |
断裂, 23°C |
4.0 |
9.0 |
% |
ASTM D638, ISO 527-2 |
断裂, 80°C |
8.0 |
15 |
% |
ASTM D638 |
断裂, 121°C |
7.0 |
6.0 |
% |
ASTM D638 |
弯曲模量 |
|
|
|
|
-40°C |
5860 |
6430 |
MPa |
ASTM D790 |
23°C |
5310 |
2400 |
MPa |
ASTM D790 |
65°C |
2400 |
-- |
MPa |
ASTM D790 |
121°C |
1930 |
-- |
MPa |
ASTM D790 |
23°C |
4770 |
2210 |
MPa |
ISO 178 |
弯曲强度 |
|
|
|
|
-40°C |
214 |
219 |
MPa |
ASTM D790 |
23°C |
172 |
101 |
MPa |
ASTM D790 |
65°C |
110 |
-- |
MPa |
ASTM D790 |
90°C |
90.0 |
-- |
MPa |
ASTM D790 |
121°C |
76.0 |
-- |
MPa |
ASTM D790 |
23°C |
160 |
65.0 |
MPa |
ISO 178 |
冲击性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
简支梁缺口冲击强度 |
|
|
|
ISO 179 |
-30°C |
5.5 |
-- |
kJ/m² |
ISO 179 |
23°C |
6.5 |
-- |
kJ/m² |
ISO 179 |
简支梁无缺口冲击强度 (23°C) |
40 |
-- |
kJ/m² |
ISO 179 |
悬壁梁缺口冲击强度 |
|
|
|
|
23°C |
59 |
-- |
J/m |
ASTM D256 |
23°C |
5.0 |
-- |
kJ/m² |
ISO 180 |
热性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
热变形温度 |
|
|
|
|
0.45 MPa, 未退火 |
217 |
-- |
°C |
ISO 75-2/B |
1.8 MPa, 未退火 |
200 |
-- |
°C |
ASTM D648 |
1.8 MPa, 未退火 |
195 |
-- |
°C |
ISO 75-2/A |
熔融峰值温度 |
220 |
-- |
°C |
ASTM D3418, ISO 3146 |
线形热膨胀系数 |
|
|
|
|
流动 |
5.0E-5 |
-- |
cm/cm/°C |
ASTM E831 |
流动 |
3.9E-5 |
-- |
cm/cm/°C |
|
横向 |
7.8E-5 |
-- |
cm/cm/°C |
|
RTI Elec |
|
|
|
UL 746 |
0.800 mm |
130 |
-- |
°C |
UL 746 |
1.50 mm |
130 |
-- |
°C |
UL 746 |
3.00 mm |
130 |
-- |
°C |
UL 746 |
6.00 mm |
130 |
-- |
°C |
UL 746 |
RTI Imp |
|
|
|
UL 746 |
0.800 mm |
95.0 |
-- |
°C |
UL 746 |
1.50 mm |
105 |
-- |
°C |
UL 746 |
3.00 mm |
105 |
-- |
°C |
UL 746 |
6.00 mm |
105 |
-- |
°C |
UL 746 |
RTI |
|
|
|
UL 746 |
0.800 mm |
105 |
-- |
°C |
UL 746 |
1.50 mm |
105 |
-- |
°C |
UL 746 |
3.00 mm |
105 |
-- |
°C |
UL 746 |
6.00 mm |
105 |
-- |
°C |
UL 746 |
电气性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
体积电阻率 |
|
|
|
|
1.50 mm |
> 1.0E+13 |
-- |
ohms·cm |
ASTM D257 |
-- |
> 1.0E+13 |
-- |
ohms·cm |
IEC 60093 |
介电强度 |
40 |
-- |
kV/mm |
IEC 60243-1 |
介电常数 |
|
|
|
IEC 60250 |
100 Hz |
3.60 |
-- |
|
IEC 60250 |
1 MHz |
3.40 |
-- |
|
IEC 60250 |
耗散因数 |
|
|
|
IEC 60250 |
100 Hz |
0.010 |
-- |
|
IEC 60250 |
1 MHz |
0.020 |
-- |
|
IEC 60250 |
可燃性 |
干燥 |
调节后的 |
单位制 |
测试方法 |
UL 阻燃等级 |
|
|
|
UL 94 |
0.800 mm |
HB |
-- |
|
UL 94 |
1.50 mm |
HB |
-- |
|
UL 94 |
3.00 mm |
HB |
-- |
|
UL 94 |
6.00 mm |
V-2 |
-- |
|
UL 94 |
注射 |
干燥 |
单位制 |
|
干燥温度 |
80.0 |
°C |
|
干燥时间 |
2.0 到 4.0 |
hr |
|
建议的最大水分含量 |
0.15 |
% |
|
加工(熔体)温度 |
250 到 290 |
°C |
|
模具温度 |
80.0 到 95.0 |
°C |
|
注塑压力 |
3.50 到 12.5 |
MPa |
|
注射速度 |
快速 |
|
|