PC/ABS德国拜耳 FR110 阻燃 V0级 光稳定性 中等流动 工程塑料
-
Covestro Bayblend® FR 110 Polycarbonate/ABS Blend PC/ABS
Polymer,Thermoplastic,ABS Polymer,Polycarbonate/ABS Alloy, Unreinforced,Polycarbonate (PC)
Covestro
产品说明:
Flame retardant grade with antimony, chlorine and bromine free, flame retardant package, good light stability.
Applications: Housings for business machines.
Information provided by Bayer.
As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.
Covestro Bayblend® FR 110 Polycarbonate/ABS Blend 物性表 工程塑料 科思创
物理性能
额定值 (公制)
额定值 (英制)
测试方法
密度
1.19 g/cc
0.0430 lb/in³
吸水率
0.70 %
0.70 %
Saturation in water
平衡吸湿
0.20 %
0.20 %
Equilibrium at 50% RH
饱和吸水率
0.70 %
0.70 %
线性成型收缩率
0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ASTM D955
熔体流动速率
20 g/10 min
@Load 5.00 kg, Temperature 240 °C
20 g/10 min
@Load 11.0 lb, Temperature 464 °F
Spiral Flow
58.0 cm
@Thickness 2.50 mm
22.8 in
@Thickness 0.0984 in
at 254°C melt temp.
机械性能
额定值 (公制)
额定值 (英制)
测试方法
洛氏硬度（R 级）
122
122
ASTM D785
极限抗拉强度
56.0 MPa
8120 psi
ASTM D638
抗张强度(屈服)
60.0 MPa
8700 psi
伸长率 (断裂)
90 %
90 %
ASTM D638
屈服伸长率
4.0 %
4.0 %
拉伸模量
2.60 GPa
377 ksi
弯曲强度
95.0 MPa
13800 psi
at 5% strain; ASTM D790
弯曲模量
2.70 GPa
392 ksi
ASTM D790
悬壁梁缺口冲击强度
7.50 J/cm
@Thickness 3.20 mm
14.1 ft-lb/in
@Thickness 0.126 in
ASTM D256
冲击试验
52.0 J
@Thickness 3.20 mm
38.4 ft-lb
@Thickness 0.126 in
Instrumented Total Impact; 3.2 mm thick, 12.5 mm dart, 75 mm clamp, 6.7 m/s; ASTM D3763
电气性能
额定值 (公制)
额定值 (英制)
测试方法
电阻率
1.00e+15 ohm-cm
1.00e+15 ohm-cm
表面电阻
>= 1.00e+15 ohm
>= 1.00e+15 ohm
介电常数
2.9
@Frequency 1e+6 Hz
2.9
@Frequency 1e+6 Hz
3.0
@Frequency 100 Hz
3.0
@Frequency 100 Hz
介电强度
30.0 kV/mm
762 kV/in
耗散因数
0.0030
@Frequency 100 Hz
0.0030
@Frequency 100 Hz
0.0080
@Frequency 1e+6 Hz
0.0080
@Frequency 1e+6 Hz
耐电弧性
60 - 120 sec
@Thickness 3.00 mm
60 - 120 sec
@Thickness 0.118 in
UL Rating PLC 6 (60-120 sec)
相比耐漏电起痕指数(CTI)
300 V
300 V
热丝引燃 (HWI)
60 - 120 sec
@Thickness 3.00 mm
60 - 120 sec
@Thickness 0.118 in
UL Rating PLC 1 (60-120 sec)
高电弧燃烧，HAI
>= 120 arcs
@Thickness 2.00 mm
>= 120 arcs
@Thickness 0.0787 in
UL Rating PLC 0 (>120 arcs)
高压电弧跟踪率，HVTR
>= 150 mm/min
@Thickness 3.00 mm
>= 5.91 in/min
@Thickness 0.118 in
UL Rating PLC 4 (>150 mm/min.)
热性能
额定值 (公制)
额定值 (英制)
测试方法
线形热膨胀系数 - 流动
76.0 µm/m-°C
@Temperature 20.0 °C
42.2 µin/in-°F
@Temperature 68.0 °F
线性热膨胀系数,横向流动
80.0 µm/m-°C
@Temperature 20.0 °C
44.4 µin/in-°F
@Temperature 68.0 °F
载荷下热变形温度(0.46 MPa)
100 °C
212 °F
载荷下热变形温度(1.8 MPa)
90.0 °C
194 °F
维卡软化温度
108 °C
226 °F
UL RTI
95.0 °C
203 °F
UL RTI，机械冲击
85.0 °C
185 °F
UL RTI，机械无冲击
85.0 °C
185 °F
可燃性(UL94)
V-0
@Thickness 1.60 mm
V-0
@Thickness 0.0630 in
极限氧指数
30 %
30 %
加工性能
额定值 (公制)
额定值 (英制)
测试方法
加工（熔体）温度
220 - 270 °C
428 - 518 °F
耐水解稳定性PC/ABS
耐水解稳定性系列PC/ABS（HAC8250R）主要应用于汽车仪表板骨架等汽车内饰产品。汽车仪表板骨架作为整个仪表板的支撑结构件，其重要性不言而喻，因此主机厂对仪表板材料提出了更苛刻的要求。目前，仪表板骨架不仅要求有良好的机械性能，加工性能，而且要有优秀的耐水解性能和热老化性能，以适应汽车在极端高温，高湿的环境下使用。
超低光泽PC/ABS
汽车内饰材料一般都有哑光的要求，这样有利于减少驾驶员的视觉疲劳，从而提高了驾驶安全性。PC/ABS的综合性能良好，但由于其表面的光泽度较高，而需要喷哑光漆等二次加工来实现哑光与美观的效果。随着汽车ELV法规的出台，需要免喷涂的环保解决方案来实现制品直接进行回收处理。免喷涂解决方案不仅可以大幅降低成本，而且可以减少喷漆过程造成的环境污染。
耐化学溶剂PC/ABS
PC/ABS的综合性能优良，但是其耐化学品性能差而容易受到比较强的化学溶剂侵蚀而导致制品开裂等缺陷。特别是当PC/ABS 制品喷涂某些车身外饰漆时，由于其溶剂的强腐蚀性，易导致制品出现应力痕，龟裂，甚至开裂。优畅锦湖针对这种情况，开发了新一代耐化学溶剂的PC/ABSHAC8265P，这种材料经过了模拟化学品溶剂的应力侵蚀，其产生裂纹的时间比普通PC/ABS 提高了3倍。
典型应用范围:
汽车内外饰：仪表板，饰柱，仪表前盖，格栅，内外饰件 2.商务设备机壳和内置部件：笔记本/台式电脑，复印机，打印机，绘图仪，显示器 3.电信，移动电话外壳，附件以及智能卡（SIM卡）： 4.电器产品，电子产品外壳，电表罩和壳体，家用开关，插头和插座，电缆电线管道 5.家用电器，如洗衣机，吹风机，微波炉内外部件等。
-